Dealing with corrosion has become a bigger part of truck maintenance since road departments began using highly aggressive de-icing salts, primarily calcium chloride and magnesium chloride, which are especially hard on ferrous metals.


Aside from body panels, corrosion is most visible on wheels, which are close to salty spray — and to observers’ eyes. Rust gets the attention of vehicle inspectors, who may assume that greater, more dangerous problems lurk underneath.

Corrosion can be headed off at purchasing time when new wheels are spec’d. Many fleets have switched to aluminum wheels, which are lighter in weight and also stand up better to salt than steel. Aluminum is not immune to corrosion, but will resist it for a considerably longer time. Resistance is even better with factory treatments that add hardness to surfaces along with an especially bright look. These include Alcoa’s Dura-Bright and Accuride’s Accu-Flange, Accu-Shield and Accu-Armor.

Where tare weight isn’t an issue, steel’s lower cost remains attractive for many users. There are treatments for new steel wheels that resist salt-induced corrosion:

  • Accuride recently introduced EverSteel, a proprietary bare-metal treatment followed by a zinc phosphate pre-treatment, with an epoxy e-coat and a Steel Armor powder coat top finish. The company guarantees it against corrosion for five years if used with Wheel Guard separators.
  • Maxion offers a Premium Powder Top Coating that starts with a phosphate coat, then white electro-deposition primer that’s baked on. Customers select the color for the top powder coat, which is also baked on. This finish lasts 2,000 hours in a standard salt-spray test, the company says.

The millions of aluminum and steel wheels already in use, however, remain susceptible to corrosion damage, and must be periodically cared for.

For aluminum wheels, Hartt Transportation in Bangor, Maine, has devised a process that concentrates on a wheel’s inner hub bore and mating surfaces that pick up rust from the steel hub and iron brake drum, says Todd Cotier, maintenance manager. Mechanics remove it with a soft abrasive attachment on a grinder and a 6-inch sander with 100-grit paper. The rest of the wheel is polished as needed. (Iron hubs and drums and steel studs and nuts also get special attention.)

Steel wheels need extra work because iron-oxide rust chemically clings to their surfaces. Members of the Technology & Maintenance Council of American Trucking Associations wrote a set of suggestions for removing the rust and retreating wheel surfaces. Recommended Practice 240A emphasizes careful inspections to find any damage that could put a wheel out of service.

One is surface wear from salt damage or overly aggressive media blasting. “If the DOT stamp or manufacturer’s identifying marks are not legible for any reason, the rim/wheel must be removed from service and scrapped,” the RP says.

Existing dirt, grease or debris should be removed prior to further inspection and removal of paint or coatings. Blasting with a combination of metal shot and grit works well for removing old powder coating. Bare-steel wheels should not be handled with bare hands, lest skin oils contaminate the surface and mar subsequent coating. The RP suggests priming with a product compatible with the chosen outer coating; powder coating holds up best to salt.

A man who had a hand in writing RP-240A is Jeff Redding, national equipment and coatings manager for IMI, a producer of tire and wheel maintenance products. IMI makes a turnkey wheel refinishing system used by tire and wheel dealers at about 200 locations in the United States. The components for this standardized Milcure system sit in-line with each other so wheels can be efficiently and consistently processed. Education in proper operation and inspection is part of the IMI support, Redding says.

A trained technician moves wheels among several steps and inspects them between each. He or she looks for imperfections, especially cracks, that render a wheel unfit for further use.  Cracks cannot be safely repaired and a cracked wheel should be scrapped.

IMI’s process includes four steps:

  • Blasting with steel abrasives to remove rust and what’s left of the coating, taking the wheel down to bare metal without damaging the surface. This is done in a blast cabinet designed to handle wheels and takes about four minutes.
  • Electrostatic powder coating is applied with a hand-held spray gun in a special booth. The powder is positively charged and air-sprayed onto the wheel, where a negative charge causes the powder to cling. Application-specific powder coatings maximize the adhesion to the wheel and resistance to premature corrosion. This takes two and a half minutes.
  • Curing in an oven for 15 minutes to a wheel temperature of 380 to 420 degrees, which liquefies and cures the powder into a hard surface.
  • Cooling for another 15 to 20 minutes, after which the wheel is ready for final inspection and palletizing with others for return to the customer.

“We have a guy here five days a week and that’s all he does – wheels,” says Larry Harmon, manager at Bob Sumerel Tire in Zanesville, Ohio, which uses the IMI process. Steady customers include major fleets as well as smaller, local operations and walk-ins.

“Our goal is 40 to 70 wheels a day,” Harmon says. “Time to do wheels varies, maybe seven minutes for blasting, then coating and baking with what we call the pizza oven.

“It lasts for several years. Salt’s hard on everything, but they hold up through that,” he says of the refinished wheels. “A lot of it’s customer care. If they wash it thoroughly, that makes a difference. When you get salt on your car, what do you do? Run it through the car wash, right? That’s what you should do with a truck.”